PTFE heat shrink tubing
Ptfe heat shrink tube combines of most advantages of common heat shrinkable tube and outstanding chemical properties of fluoropolymer. This kind of heat shrink tubing consist of 100% PTFE material, meanwhile it is the best of the entire fluoropolymer heat shrink tubing family, provide high temperature and chemical resistance with a low friction rating and a very low level of moisture absorption. when the tube totally shrunk, it need high temperature.
What's special of our teflon heat shrink tubing
1.1.7:1 or 4:1 shrink ratio
2.Exceptional heat resistance
3.Chemically inert
4.Superior dielectric strength
5.Lowest coefficient of friction
6.Self-extinguishing
7.Non-wetting
Physical properties
| Material | PTFE |
| Working temperature |
-80℃~+260℃ |
|
Shrinkage temperature |
320℃~+400℃ |
|
Longitudinal shrinkage |
≤5% |
|
Hardness |
85 |
|
Voltage |
30kv/mm |
| Shrink tool |
heat-gun, oven |
| Certificated | Rohs |
| Size range |
0.7mm~12mm |
| Standard color | Transparents |
Application
PTFE heat shrink tubing widely used in military applications, industrial, biomedical, chemical and analytical sciences and printing industry.
Specification
|
1.7:1 Shrink Ratio |
|||||
| Part No |
As supplied(mm) |
After recovery(mm) | Packing Length | ||
| ID | Thickness | ID | Thickness | ||
| MJ-HST-PTFE-0.5 |
0.7±0.2 |
0.15±0.05 |
≤0.40 |
0.25±0.05 |
200 m/roll |
|
MJ-HST-PTFE-1.0 |
1.0±0.2 |
0.15±0.05 |
≤0.50 |
0.25±0.05 |
200 m/roll |
|
MJ-HST-PTFE-1.5 |
1.5±0.2 |
0.20±0.05 |
≤0.90 |
0.25±0.05 |
200 m/roll |
|
MJ-HST-PTFE-2.0 |
2.0±0.2 |
0.20±0.05 |
≤1.30 |
0.30±0.05 |
200 m/roll |
|
MJ-HST-PTFE-2.5 |
2.5±0.2 |
0.20±0.05 |
≤1.50 |
0.30±0.05 |
200 m/roll |
|
MJ-HST-PTFE-3.0 |
3.0±0.2 |
0.20±0.05 |
≤1.80 |
0.30±0.05 |
200 m/roll |
|
MJ-HST-PTFE-3.5 |
3.5±0.2 |
0.20±0.05 |
≤2.00 |
0.30±0.05 |
200 m/roll |
|
MJ-HST-PTFE-4.0 |
4.0±0.3 |
0.20±0.05 |
≤2.50 |
0.30±0.05 |
200 m/roll |
|
MJ-HST-PTFE-4.5 |
4.5±0.3 |
0.20±0.05 |
≤2.80 |
0.30±0.05 |
200 m/roll |
|
MJ-HST-PTFE-5.0 |
5.0±0.3 |
0.20±0.05 |
≤3.00 |
0.30±0.05 |
200 m/roll |
|
MJ-HST-PTFE-6.0 |
6.0±0.3 |
0.25±0.05 |
≤3.80 |
0.38±0.05 |
100 m/roll |
|
MJ-HST-PTFE-7.0 |
7.0±0.3 |
0.25±0.05 |
≤4.00 |
0.38±0.05 |
100 m/roll |
|
MJ-HST-PTFE-8.0 |
8.0±0.3 |
0.25±0.05 |
≤4.80 |
0.38±0.05 |
100 m/roll |
|
MJ-HST-PTFE-9.0 |
9.0±0.3 |
0.25±0.05 |
5.00 |
0.38±0.05 |
100 m/roll |
|
MJ-HST-PTFE-10.0 |
10.0±0.3 |
0.25±0.05 |
≤6.00 |
0.38±0.05 |
100 m/roll |
|
MJ-HST-PTFE-12.0 |
12.0±0.3 |
0.25±0.05 |
≤7.00 |
0.38±0.05 |
100 m/roll |
|
4:1 Shrink Ratio |
|||||
| Part No |
As supplied(mm) |
After recovery(mm) |
Packing Length | ||
| ID | Thickness | ID | Thickness | ||
|
MJ-HST-PTFE-4-2.0 |
2.0±0.25 |
0.06±0.02 |
≤0.50 |
0.20±0.05 |
100 m/roll |
|
MJ-HST-PTFE-4-2.5 |
2.5±0.25 |
0.06±0.02 |
≤0.65 |
0.20±0.05 |
100 m/roll |
|
MJ-HST-PTFE-4-3.0 |
3.0±0.25 |
0.06±0.02 |
≤0.75 |
0.20±0.05 |
100 m/roll |
|
MJ-HST-PTFE-4-3.5 |
3.5±0.25 |
0.06±0.02 |
≤0.88 |
0.20±0.05 |
100 m/roll |
|
MJ-HST-PTFE-4-4.0 |
4.0±0.25 |
0.06±0.02 |
≤1.00 |
0.20±0.05 |
100 m/roll |
|
MJ-HST-PTFE-4-4.5 |
4.5±0.25 |
0.06±0.02 |
≤1.15 |
0.20±0.05 |
100 m/roll |
|
MJ-HST-PTFE-4-5.0 |
5.0±0.25 |
0.06±0.02 |
≤1.25 |
0.20±0.05 |
100 m/roll |